Título : Assessment of the susceptibility of lacquered tinplate cans to corrosion in different solutions using electrochemical methods
Otros títulos : Evaluación de la susceptibilidad a la corrosión de recipientes de hojalata en diferentes soluciones usando técnicas electroquímicas
Autor : Calderón Gutiérrez, Jorge Andrés
Buitrago, Carmen P.
Palabras clave : Tinplate
Electrochemical techniques
Corrosion in containers
Corrosión electroquímica
Contenedores
Corrosión de hojalata
Electroquímica
Fecha de publicación : 2007
Editorial : Universidad de Antioquia, Facultad de Ingeniería
Citación : J. A. Calderón y C. P. Buitrago, "Assessment of the susceptibility of lacquered tinplate cans to corrosion in different solutions using electrochemical methods," Rev. Fac. Ing. Univ. Antioquia, no. 42, pp. 30-37, 2007.
Resumen: La corrosión de recipientes fabricados en hojalata expuestos a diferentes soluciones fue evaluada usando técnicas electroquímicas. Los recipientes con y sin la aplicación de barniz fueron expuestos a diferentes soluciones. La susceptibilidad a sufrir corrosión se evaluó utilizando voltametría cíclica, curvas de polarización y espectroscopía de impedancia electroquímica. La posibilidad de formación de películas pasivas en la superficie de los recipientes se evaluó según la histéresis presente en el primer ciclo de las medidas de voltametría. Las curvas de polarización revelaron que el comportamiento del recubrimiento de estaño puede cambiar de anódico a catódico según la naturaleza de la solución en contacto con el recipiente, alertando sobre el riesgo de corrosión localizada. Mediante impedancia electroquímica se evaluó el efecto del uso de un aditivo en las soluciones o productos empacados en dos recipientes. Las medidas de impedancia mostraron un efecto perjudicial del aditivo utilizado y una rápida aparición de procesos corrosivos cuando se usó la solución modificada con el aditivo.
Abstract : Corrosion of lacquered tinplate cans in different solutions was assessed using electrochemical methods. Samples with and without lacquer coating were exposed to different solutions and their susceptibility to corrosion was evaluated using cyclic voltammetry, Tafel curves and electrochemical impedance spectroscopy. The possible formation of a passive layer on the container surface was evaluated according to the kind of hysteresis presented in the first cycle of voltammeter measurements. Tafel plots showed how the behavior of the tin layer can change from anodic to cathodic depending on the nature of the solution in contact with it, revealing the risk of localized corrosion. The effect of one additive in the solutions on the electrochemical performance containers was evaluated by electrochemical impedance. The impedance showed a deleterious effect of the additive, and corrosion processes appeared more quickly in containers packed with solutions modified with additive.
Grupo de INV. : Centro de Investigación, Innovación y Desarrollo de Materiales - CIDEMAT
URI : http://hdl.handle.net/10495/4163
ISSN : 01206230
24222844 E
Aparece en las colecciones: Otras Investigaciones IT

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
CalderonJorge_2007_SusceptibilityLacqueredElectrochemical.pdfArtículo de Revista1,23 MBAdobe PDFVisualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons

 


Gestión de T.I. /Sistema de Bibliotecas / Universidad de Antioquia / Cl. 67 Nº 53 - 108 - Bloque 8 Conmutador: 219 51 51- 219 51 40 comunicacionessistemadebibliotecas@udea.edu.co Medellín - Colombia