Título : Sulfuros másicos obtenidos a partir de óxidos mixtos de alta área específica como catalizadores de hidrotratamiento
Otros títulos : Unsupported sulfides obtained from high specific area mixed oxides as hydrotreating catalysts
Autor : Amaya Bustos, Sandra Liliana
Licea Fonseca, Yordy Enrique
Salamanca Guzmán, Maurin
Faro, Arnaldo
Echavarría Isaza, Adriana Patricia
Palacio Santos, Luz Amparo
Palabras clave : Hidrodesulfuración
Hidrogenación
Síntesis hidrotérmica
Fecha de publicación : 2010
Editorial : Universidad de Antioquia, Facultad de Ingeniería
Citación : S. L. Amaya et al, "Sulfuros másicos obtenidos a partir de óxidos mixtos de alta área específica como catalizadores de hidrotratamiento", Rev. Fac. Ing. Univ. Antioquia, no. 56, pp. 58-67, 2010.
Resumen: Se prepararon materiales bimetálicos Ni-Mo, Co-Mo y Co-W por medio coprecipitación y Ni-W mediante síntesis hidrotérmica. La caracterización por difracción de rayos X (XRD) confirmó la formación de fases laminares fy en los molibdatos, mientras que los tungstatos exhibieron fases fy semi-cristalina y wolframita. Los análisis térmicos (TGA y DTA) de estos materiales mostraron transiciones de fase alrededor de 400°C, excepto el CoMofy a 350°C; a estas temperaturas se calcinaron los precursores bimetálicos para producir óxidos mixtos, los cuales presentaron altas áreas específicas, si se comparan con materiales análogos reportados por rutas de síntesis diferentes. Los análisis de espectroscopía infrarroja con transformada de Fourier (FTIR) confirmaron la obtención de las fases en las especies precursoras y calcinadas. La actividad catalítica de los óxidos mixtos sulfurados fue evaluada simultáneamente en las reacciones de hidrodesulfuración (HDS) de dibenzotiofeno (DBT) e hidrogenación (HYD) de tetralina. Los resultados mostraron un comportamiento similar a los catalizadores comerciales y se observó además el efecto del promotor (Ni y Co) en las reacciones.
Abstract : Several bimetallic Ni-Mo, Co-Mo and Co-W materials were prepared by co-precipitation and a Ni-W material through hydrothermal synthesis. The characterization by X-ray diffraction (XRD) of molybdates confirmed the formation of layered fy phase, while the tungstates showed both fy semicrystalline and wolframite. The thermal analyses (TGA and DTA) of these materials showed phase transition around 400°C, excepting by CoMofy to 350°C; these temperatures were selected to calcine the bimetallic precursors to obtain mixed oxides, which exhibited high specific surface areas as compared to analogous materials reported by different synthesis pathways. The Fourier transformed infrared spectroscopy (FTIR) confirmed the phase formation of the species in precursors and mixed oxides. The catalytic activity of the sulfurated mixed oxides was simultaneously evaluated in the hydrodesulphurization (HDS) of dibenzotiophene (DBT) and the hydrogenation (HYD) of tetraline. Results showed a similar behavior to commercial catalysts. The effect of promotors (Ni and Co) is discussed.
Grupo de INV. : Catalizadores y Adsorbentes
Química de Recursos Energéticos y Medio Ambiente
URI : http://hdl.handle.net/10495/5460
ISSN : 01206230
24222844 E
Aparece en las colecciones: CIEN (Centro de Investigaciones en Ciencias Exactas y Naturales)

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
AmayaSandra_2010_SulfurosMasicosObtenidos.pdfArtículo de Revista2,11 MBAdobe PDFVisualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons

 


Gestión de T.I. /Sistema de Bibliotecas / Universidad de Antioquia / Cl. 67 Nº 53 - 108 - Bloque 8 Conmutador: 219 51 51- 219 51 40 comunicacionessistemadebibliotecas@udea.edu.co Medellín - Colombia