Síntesis por vía hidrotérmica de un material tipo hidrotalcita basado en manganeso y cromo

Abstract

ABSTRACT: In this work were synthesized by hydrothermal method, hydrotalcite materials based in Mn and Cr, under different conditions of temperature (80-150°C). These solids were characterized by Xray diffraction, and it was found the presence of some impurities belonging to manganese oxides. From this analysis it was determined that the best phase hydrotalcite was obtained at a temperature of 120°C, thus this solid was calcined to obtain a mixture of oxides, and then used as a catalyst in the oxidative dehydrogenation reaction of propane.

RESUMEN: En este trabajo se sintetizaron, por el método hidrotérmico, materiales tipo hidrotalcita basados en Mn y Cr, bajo diferentes condiciones de temperatura (80-150ºC). Dichos sólidos fueron caracterizados por difracción de rayos X, y se encontró que había presencia de algunas impurezas pertenecientes a óxidos de manganeso. A partir de este análisis se determinó que la mejor fase hidrotalcita se obtuvo a una temperatura de 120ºC, por ende dicho sólido fue calcinado para obtener una mezcla de óxidos, y posteriormente usarlo como catalizador en la reacción de deshidrogenación oxidativa de propano.