Corrosion related iron oxides : Cu, Mn and Cr doped hematite

Abstract

ABSTRACT: We have obtained Cu, Mn, and Cr doped hematites, by a thermal treatment of doped goethites at 500 and 880 °C in air for 24 h. The goethites were prepared in the laboratory from iron chloride solutions in the presence of Cu^"^, Mn^^, and Cr^^ ions. The samples are characterized by Mossbauer spectroscopy and X-ray diffraction. It is found that at 500 °C all the goethites have transformed into hematites. However, the thermal treatment at 880 °C produces hematites with better crystallinity.

RESUMEN: Hemos obtenido hematitas dopadas con Cu, Mn y Cr, por un tratamiento térmico de goethitas dopadas a 500 y 880 °C en aire durante 24 h. Las goethitas fueron preparadas en el laboratorio a partir de soluciones de cloruro de hierro en presencia de iones de Cu2+, Mn2+ y Cr3+. Las muestras fueron caracterizadas por espectroscopia Mössbauer y difracción de rayos X. Se encontró que a 500 °C todas las goethitas se han transformado a hematitas. Sin embargo, el tratamiento térmico a 880 °C produce hematitas con mejor cristalinidad.