Título : Effect of soda ASH (NA2CO3) and limestone (CaCO3) reduction on mechanical and physical properties of soda-lime-silica glasses used in the manufacturing of containers and flat glass
Otros títulos : Efecto de la reducción de soda ASH (NA2CO3) y caliza (CaCO3) sobre las propiedades mecánicas y físicas de vidrios de soda-cal-sílice usados en la manufactura de envases de vidrio y vidrio plano
Autor : Franco, David
Zapata Gallego, Natalia Trinidad
Montoya, Victor
Jiménez, Camilo
López Gómez, María Esperanza
Palabras clave : Caliza
Composición química
Industria de envases de vidrio
Vidrio
Fecha de publicación : 2017
Editorial : Universidad de Antioquia, Facultad de Ingeniería
Citación : Franco, D., Zapata, N., Montoya, V., Jiménez, C., & López, M. E. (2017). Effect of soda ASH (NA2CO3) and limestone (CaCO3) reduction on mechanical and physical properties of soda-lime-silica glasses used in the manufacturing of containers and flat glass. Revista Colombiana de Materiales, 10, 31-42
Resumen: La Soda ASH (Na2CO3) es uno de los componentes más importantes para producir vidrio ya que este material es capaz de romper la red de SiO2 y por lo tanto determina importantes propiedades, sin embargo, dicha materia prima también es muy costosa y existe un paradigma al interior de la industria del vidrio concerniente a posibles problemas que se pueden presentar cuando hay disminuciones de Na2O. En este orden de ideas, una disminución progresiva y metodológica de Soda ASH fue desarrollada sobre vidrios fabricados acorde a un diseño de experimentos (DOE), pretendiendo medir y analizar diferentes propiedades mecánicas, físicas y químicas acorde con normas ASTM y procedimientos industriales, obteniendo como resultado cambios estadísticamente no significativos en las propiedades medidas cuando hay disminuciones de hasta el 2.64% en peso de Na2O, lo cual permite pensar en estas disminuciones como una opción para los problemas de la industria del vidrio relacionados con este mineral.
Abstract : Soda ASH (Na2CO3) is one of the most important components to produce glass since this material is able to break the SiO2 network and therefore it determines important properties, however it is also so expensive and there is into the glass industry a paradigm regarding possible issues involved with the Na2O decreases. In this order of ideas, a progressive and methodological decrease of Soda ASH was performed over glasses manufactured following a design of experiments (DOE), aiming to measure and to analyze different mechanical, physical and chemical properties according to the respective ASTM standards or industrial procedures, obtaining as a result non-significant statistical changes in all properties measured when there are decreases up to 2.64 wt. % of Na2O, which allows to think about these decreases as an option for the glass industry issues related to this ore.
Grupo de INV. : GIMACYR - Grupo de Investigación en Materiales y Recubrimientos Cerámicos
URI : http://hdl.handle.net/10495/7747
ISSN : 22561013
Aparece en las colecciones: CIA (Centro de Investigaciones Ambientales y de Ingeniería)

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
FrancoDavid_2017_Effectsodalimestone.pdfArtículo de Revista1,71 MBAdobe PDFVisualizar/Abrir


Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons

 


Gestión de T.I. /Sistema de Bibliotecas / Universidad de Antioquia / Cl. 67 Nº 53 - 108 - Bloque 8 Conmutador: 219 51 51- 219 51 40 comunicacionessistemadebibliotecas@udea.edu.co Medellín - Colombia